Engineering Plastic Functional

Buy Now

xCE-White – Functional

High performance polymer for producing end-use plastic parts and injection molding tools in minutes. Nexa3D’s new material is the fastest single cure polymer boasting higher flexural strength compared to those typically achieved only in dual cure cyanate ester resins. xCE-White has excellent isotropic properties and exhibit long-term environmental stability.

xCE-White is used to produce injection molding tools for a wide range of thermoplastic polymers including PP, PE, HDPE and PETG. Molds printed from xCE-White were successfully injected hundreds of times at temperatures between 230°C and 280°C without any visible mold temperature degradation or adhesion, and without the use of any mold release agents.

Unique Features
  • Fastest single cure polymer for heavy-duty parts and injection molding tools
  • Lightweight yet sturdy with inherent functionality to withstand load, pressure & temperature
  • High flexural strength comparable only to dual-cure cyanate ester resins
  • Isotropic properties for automotive, electronics and industrial components
Applications
  • Automotive parts, automation & robotics assemblies
  • Serial production of industrial components
  • Fast Production of functional injection molding tools
Mechanical Properties
Measurement Condition Metric Imperial
Tensile Strength

ASTM D638

69 ± 2 MPa

9932 ± 324 psi

Tensile Modulus ASTM D638

2.84 ± 0.13 GPa

412 ± 18 kpsi

Elongation at Break ASTM D638

8.0 ± 0.4%

8.0 ± 0.4%

Flexural Strength ASTM D790

135 MPa

19.6 kpsi

Flexural Modulus

ASTM D79

3.25 GPa

471 ksi
Notched Izod Impact Strength

ASTM D256

20 J/m 0.33 ft-lbs/in
Glass Transition

DMA, E”

128°C 262°F
Hardness

ASTM D2240

89 89

 

 

Download Safety Data Sheet

Download Technical Data Sheet


Buy Now

xCE-Black  – Functional

High performance polymer for producing end-use plastic parts and injection molding tools in minutes. Nexa3D’s new material is a single cure polymer that delivers higher flexural strength compared to those typically achieved only in dual cure cyanate ester resins. xCE-Black has excellent isotropic properties and exhibit long-term environmental stability.

xCE-Black is used to produce injection molding tools for a wide range of thermoplastic polymers including PP, PE, HDPE and PETG. Molds printed from xCE-Black were successfully injected hundreds of times at temperatures between 230°C and 280°C without any visible mold temperature degradation or adhesion, and without the use of any mold release agents.

Unique Features
  • High performance accurate
  • High Flexure Strength
  • High Temperature resistance
Applications
  • Automotive under hood and interior parts
  • Serial production of small industrial parts
  • Production of injection molding inserts
Mechanical Properties
Measurement Condition Metric Imperial
Tensile Strength

ASTM D638

69 ± 2 MPa

9932 ± 324 psi

Tensile Modulus ASTM D638

2.84 ± 0.13 GPa

412 ± 18 kpsi

Elongation at Break ASTM D638

8.0 ± 0.4%

8.0 ± 0.4%

Flexural Strength ASTM D790

135 MPa

19.6 kpsi

Flexural Modulus

ASTM D79

3.25 GPa

471 ksi
Notched Izod Impact Strength

ASTM D256

20 J/m 0.33 ft-lbs/in
Glass Transition

DMA, E”

128°C 262°F
Hardness

ASTM D2240

89 89

 

 

Download Material Data Sheet